NanoMetals :-
Along with listed NanoMetals, many other metals were produced as trial batches in nanosizedform, e.g. Stainless steel, Sn, Mn, Rare Earth Metals, W, Mo, V, Ag, Pt, Ir, Au. The same as in case of NanoCeramics, we are ready to produce almost any nanometal,also from material of customers.
Copper
Cu-nanopowder suspension in oil
Average particle size: 40±5 nm
Specific surface area: 15±5 m2/g
Controlled admixtures, %: metal impurities < 0.1 including Fe < 0.02
Oil: 20 wt.%, Oleic acid (stabilizer): 3 wt.%
Specific surface area: 15±5 m2/g
Controlled admixtures, %: metal impurities < 0.1 including Fe < 0.02
Oil: 20 wt.%, Oleic acid (stabilizer): 3 wt.%
Available in : 5g , 25g , 100g Pack Sizes
Cu-nanopowder suspension in ethanol
Average particle size: 40±5 nm
Specific surface area: 15±5 m2/g
Controlled admixtures, %: metal impurities < 0.1 including Fe < 0.02
Ethanol: 30% by total weight, Oleic acid (stabilizer): 3 wt.%
Specific surface area: 15±5 m2/g
Controlled admixtures, %: metal impurities < 0.1 including Fe < 0.02
Ethanol: 30% by total weight, Oleic acid (stabilizer): 3 wt.%
Available in : 5g , 25g , 100g Pack Sizes
Cu-nanopowder, dry
Average particle size: 40±5 nm
Oleic acid (stabilizer): 3 wt.%
Same as above, but as a dry powder
Oleic acid (stabilizer): 3 wt.%
Same as above, but as a dry powder
Available in : 5g , 25g , 100g Pack Sizes
Copper-Tin alloy
Purity: > 97.0 %
Particle shape: spheric
Average particle size: 70 - 80 nm. Particle size full range: 5 - 250 nm
Specific surface area: > 10 m2/g
Bulk density: > 0.8 g/cm3
Controlled admixtures, %: Fe < 0.1; W < 0.2
Particle shape: spheric
Average particle size: 70 - 80 nm. Particle size full range: 5 - 250 nm
Specific surface area: > 10 m2/g
Bulk density: > 0.8 g/cm3
Controlled admixtures, %: Fe < 0.1; W < 0.2
Available in : 5g , 25g Pack Sizes
Gold Nanoparticles
Colloidal solution in water, 0.05 mg/mL
Average particle size: 20±3 nm pH ca. 8,0
Average particle size: 20±3 nm pH ca. 8,0
Available in : 10ml , 100ml Pack Sizes
|