Nano Diamonds :-
All types of nanodiamonds and nanographite / nanodiamonds mixtures are produced by
controlled detonation synthesis followed by purification procedures.
We are ready to change product quality in case of special requirements.
Graphite / Diamond Nano-Mixture
The most native, raw, just after detonation synthesis.
Average diamond primary particle size: 4 nm
Diamond content: min. 20%
Ash content: < 6%
Diamond content: min. 20%
Ash content: < 6%
Available in : 5g , 25g , 100g Pack Sizes
Graphite / Diamond Nano-Mixture
Purified from metallic and organic impurities
Average diamond primary particle size: 4 nm
Diamond content: min. 20%
Ash content: < 0.3%
Diamond content: min. 20%
Ash content: < 0.3%
Available in : 5g , 25g , 100g Pack Sizes
Nano Diamonds, Purified, Grade G
Enhanced suspension stability in water
Specific surface (BET): min. 290-360 m2/g
Diamond phase content: min. 87%
Non-diamond carbon content: max. 6%
Impurities, %: Fe < 1,2; Ca+Zn+Cr+Ni+Cu+Mn: < 2
Losses at tempering: < 3%
Ash content: < 6%
Average cluster size: ca. 4 nm
Specific surface (BET): min. 290-360 m2/g
Diamond phase content: min. 87%
Non-diamond carbon content: max. 6%
Impurities, %: Fe < 1,2; Ca+Zn+Cr+Ni+Cu+Mn: < 2
Losses at tempering: < 3%
Ash content: < 6%
Average cluster size: ca. 4 nm
Available in : 1g , 5g , 25g , 100g Pack Sizes
NanoPure-G,grade G
Nanodiamonds aqueous suspension,
Most native 4 wt.% aqueous suspension of nanodiamonds, type PL-D-G.
The nanodiamonds are preserved in the most dispersed form.
The nanodiamonds are preserved in the most dispersed form.
Available in : 10ml , 50ml , 100ml Pack Sizes
Nano Diamonds, Purified, Grade G01
Enhanced suspension stability in water
Bulk density: 0.69 g/cm3
Average cluster size: ca. 4 nm
Specific surface (BET): min. 350 m2/g
Non-diamond carbon content: traces
Controlled admixtures, %: Fe < 0.3; Cu < 0.01;
Zn < 0.01; Mn < 0.01; Si+Cr+Ca+Ti < 0.01
Losses at tempering: max. 2.4%
Ash content: <1.4%; Picnometric density: 3.18 g/cm3
Zeta potential: -50 ± 5 mV
Average cluster size: ca. 4 nm
Specific surface (BET): min. 350 m2/g
Non-diamond carbon content: traces
Controlled admixtures, %: Fe < 0.3; Cu < 0.01;
Zn < 0.01; Mn < 0.01; Si+Cr+Ca+Ti < 0.01
Losses at tempering: max. 2.4%
Ash content: <1.4%; Picnometric density: 3.18 g/cm3
Zeta potential: -50 ± 5 mV
Available in : 1g , 5g , 25g , 100g Pack Sizes
NanoPure-G01 ,grade G01
Nanodiamonds aqueous suspension
Most native 4 wt.% aqueous suspension of nanodiamonds, type PL-D-G01.
The nanodiamonds are preserved in the most dispersed form..
Available in : 10ml , 50ml , 100ml Pack Sizes
Nanodiamonds
positively charged, aq. suspension
Aqueous suspension with 10 % of modified G01 nanodiamonds
Nanodiamonds with the surface modified by polyelectrolyte electrostatic adsorption. Zeta potential: +50 ± 5 mV
Nanodiamonds with the surface modified by polyelectrolyte electrostatic adsorption. Zeta potential: +50 ± 5 mV
Available in : 10ml , 50ml Pack Sizes
Nano Diamonds : extra-pure
Purity: >99%
Ash content: < 0.1%
Available in : 1g , 10g Pack Sizes
Single-Digit NanoDiamonds (SDND)
Forms transparent stable colloidal solution of nanodiamonds in water and many polar
organic solvents. Free of additives and milling impurities.
Produced by chemical desintegration. Aqueous 5% solution.
Diamond crystallite size: 3.5-5.2 nm
Specific surface: 320-350 m2/g
Particle size (DLS): 5-15 nm
Ash content: <0.4%
Can also be supplied in DMF, GBL, EG. Ask for quotation.
Produced by chemical desintegration. Aqueous 5% solution.
Diamond crystallite size: 3.5-5.2 nm
Specific surface: 320-350 m2/g
Particle size (DLS): 5-15 nm
Ash content: <0.4%
Can also be supplied in DMF, GBL, EG. Ask for quotation.
Available in : 20ml, 200ml , 1000ml Pack Sizes
|